Thermochemical surface hardening is used to overcome the weak mechanical performance of austenitic and duplex stainless steels. Both low-temperature carburizing and nitrocarburizing can improve the hardness, wear, galling, and cavitation resistance, while maintaining their good corrosion resistance. Therefore, it is crucial to not form chromium-rich precipitates during hardening as these can deteriorate the passivity of the alloy. The hardening parameters, the chemical composition of the steel, and the manufacturing route of a component determine whether precipitates are formed. This article gives an overview of suitable alloys for low-temperature surface hardening and the performance under corrosive loading.
The project aims for the development of a new material system from high tensile stainless steel wires as net material with environmentally compatible antifouling properties for off-shore fish farm cages. Therefore, current net materials from textiles (polyamide) shall be partially replaced by high strength stainless steel in order to have a more environmentally compatible system which meets the more severe mechanical loads (waves, storms, predators (sharks)). With a new antifouling strategy current issues like reduced ecological damage (e.g. due to copper disposal), lower maintenance costs (e.g. cleaning) and reduced durability shall be resolved.
Mechanical properties after stretching testings were calcu-lated and experimentally determined via Tempcore method for bar core, bar surface and whole bar cross section. It was displayed on the base of experiments and imitating simulation that deformation in core and surface areas of a bar are equal and therefore influence of structural parameters in the core area is principally decisive for initiating of neck forming in the surface area. The results showed that resistance to destruction of martensite surface layer has rather less effect on bar properties in general in comparison with previous investigations. It is concluded that improvement of core structure quality can help to lower brittleness of the whole bar. It was also proved that used techniques provide good concordance between the obtained results and experimental data. Therefore, the additivity rule for structural components can be used successfully for determination of whole bar parameters, taking into account thickness of surface layer that can be measured easily using hardness sensor. It will simplify practically quality control of products.