- Aquaculture (1)
- Austenitic stainless steels (1)
- Corrosion Resistance (1)
- Corrosion resistance (1)
- Duplex stainless steel (1)
- Dynamic testing plant (1)
- Dynamic tests (1)
- Espanded austenite, Magnetic force microscopy, Low temperature carburisation, Ferrofluid (1)
The project aims for the development of a new material system from high tensile stainless steel wires as net material with environmentally compatible antifouling properties for off-shore fish farm cages. Therefore, current net materials from textiles (polyamide) shall be partially replaced by high strength stainless steel in order to have a more environmentally compatible system which meets the more severe mechanical loads (waves, storms, predators (sharks)). With a new antifouling strategy current issues like reduced ecological damage (e.g. due to copper disposal), lower maintenance costs (e.g. cleaning) and reduced durability shall be resolved.
Hot isostatic pressing (HIP) allows the production of complex components geometry. Generally, a high quality of the components is achieved due to the well managed composition of the metal powder and the non-isotropic properties. If a duplex stainless steel is produced, a heat treatment after the HIP-process is necessary to remove precipitations like carbides, nitrides and intermetallic phases. In a new process, the sintering step should be combined with the heat treatment. In this case a high cooling rate is necessary to avoid precipitations in duplex stainless steels. In this work, the influence of the HIP-temperature and the wall thickness on corrosion resistance, microstructure and impact strength were investigated. The results should help to optimize the process parameters like temperature and cooling rate. For the investigation, two HIP-temperatures were tested in a classical HIP-process step with a defined cooling rate. An additional heat treatment was not conducted. The specimens were cut from different sectors of the HIP-block. For investigation of the corrosion resistance, the critical pitting temperature was determined with electrochemical method according to EN ISO 17864. An impact test was used to determine the impact transition temperature. Metallographic investigations show the microstructure in the different sectors of the HIP-block.
Improving the tribological properties of Stainless Steels by low-temperature surface hardening
(2022)
This paper compares the surface morphology of differently finished austenitic stainless steel AISI 316L, also in combination with low temperature carburization. Milled and tumbled surfaces were analyzed by means of corrosion resistance and surface morphology. The results of potentiodynamic measurements show that professional grinding operations with SiC and Al2O3 always lead to a better corrosion resistance of low temperature carburized surfaces compared to the untreated reference in the used acidified chloride solution. Big influence on the corrosion resistance of vibratory ground or tumbled surfaces has the amount of plastic deformation while machining, that has to be kept low for austenitic stainless steels. Due to the high ductility, plastic deformation can lead to the formation of meta stable pits that can be initiation points of corrosion. The formation of meta stable pits can be aggravated by low temperature diffusion processes.